It will be seen, therefore, that ultramarine essentially consists of alumina, silica, soda, and sulphur, and may be regarded as a sodium aluminium sulphate, in combination either with polysulphide of sodium alone, or with a polysulphide and a polythionate of sodium. Clement and Desormes believe that the iron in lazulite (lapis lazuli) is an accidental impurity, and is neither essential to the mineral itself nor to the ultramarine derived from it. There is still some doubt on this point, however, many eminent chemists holding the opinion that iron is a necessary constituent of ultramarine blue. Natural ultramarine has been almost entirely replaced by the artificial product, since methods have been devised for the manufacture of the latter on a large scale. The possibility of preparing artificial ultramarine suggested itself in a curious manner. About seventy years ago a French alkali maker noticed the occasional appearance of a blue coloured substance in his soda furnace. On analysis, Vauquelin found the substance to have the same chemical composition as lapis lazuli, and this incident led him to believe that ultramarine might be built up from its elements. Several years passed away before Guimet succeeded in manufacturing artificial ultramarine on anything like a large scale, but Gmelin is said to have prepared it in small quantity half a dozen years previously. There are four varieties of artificial ultramarine: (1) the pure deep blue, equal in colour to average native ultramarine; (2) pale blue; (3) violet or pink ultramarine; (4) green ultramarine. The latter is obtained in the first stage of the ultramarine manufacture, being the result of incomplete ignition of the materials employed. Ultramarine is generally manufactured by one of the following processes:--(_a_) “Sulphate”; (_b_) “Soda”; (_c_) “Silica.” (_a_) “_Sulphate_” _Ultramarine_.--This may be prepared from sulphate of soda (Glauber’s salt), charcoal, and kaolin (china clay). The materials should be as free as possible from iron, and it has been found that clay having approximately the formula Al_{2}O_{2} (SiO_{2})_{2} gives the best results. The clay and sulphate of soda must be thoroughly calcined. They are then intimately mixed with charcoal in the following proportions:-- Per cent. Clay 48·3 Sulphate of soda 43·5 Charcoal 8·2 ----- 100·0 Sometimes a portion of the sulphate of soda is omitted, and some carbonate of soda and sulphur added instead. The composition of the mixture then becomes:-- Per cent.