plaster of Paris, is made to adhere to a piece of machinery placed directly above the other plate, and is so situated, with respect to this latter, that the two surfaces are perfectly parallel one to the other. It should be here mentioned, that the side of the plate which touches the table is always rough, and has no polish, while that over which the roller is passed is slightly undulating, and has a bright polish similar to that of a sheet of blown glass, and which is technically known as "fire" polish. The machine to which the upper plate is attached is so arranged that, when set in motion, it causes it to move in just the same direction that a plate would do if moved by the human arm; this is therefore called an elbow motion. Boys stand by the sides of the two plates, and throw fine sand and water on the lower one, so that the opposed surfaces mutually grind one another, and when this process is completed on one side, they are reversed, and the same operation is performed on the other side. The plates have now the appearance of ground glass, and the surfaces are further ground by fine emery powder, which causes them to be much smoother and more ready for the final polishing. Formerly this was entirely done by hand, women generally being the operators, and oxide of iron, called crocus, mixed with water, the material employed for polishing. Now, however, a more rapid and perfect method is adopted by the use of machinery. A table is prepared which moves from side to side, giving to the plate a lateral motion; and above is a beam, in which holes are drilled at intervals, through which short iron rods, nearly an inch in diameter, pass. On these are padded iron buffers, covered on their under surface with leather; while, pressing down these rods, and therefore the buffers, are springs, which act with considerable force, but which are able to yield to pressure caused by any inequality over which the buffers may pass. The glass plate is fixed upon this table, and its upper surface is exposed to the action of the buffers, while oxide of iron, in a very fine state of division and mixed with water, is allowed to come upon its surface. The glass travelling from side to side is rubbed by the buffers in a lateral direction, and has also a longitudinal motion, so that every portion of it is rubbed equally. If any inequalities occur on the glass, the springs which press down the buffers give way and allow them to rise over it, and this process is continued for some time, until at last the plate receives the polish so characteristic of plate glass. It is then removed from the table and examined by skilled persons, and whatever defects can be removed by hand, are remedied.