M. Brongniart has lately made many experiments on the subject of staining glass. The colours, however, are the same as we noticed. A green glass may be made by putting on one side of the glass a blue, and on the other a yellow. A black glass may be made by a mixture of blue with the oxides of manganese and iron. Painting on glass is an ancient art. When pieces of old painted glass are examined, they have always on one side a transparent red _varnish_ burnt into them. The moderns, however, excel in this art. Glass is not acted upon by the acids, except the fluoric or hydrofluoric. Hence the acid of Derbyshire spar, which is a fluate of lime, is used for etching on glass, in the same manner as nitric acid is, on copper. Fluoric acid, a compound of fluorine and hydrogen, is decomposed during this action, and is changed, by the union of its fluorine with silicon, into the silicated fluoric acid. When a quantity of alkali is used just sufficient to fuse silica, glass is the result; but when the quantity is greater, as three or four to one, the fused mass is soluble in water, and then forms the silicated alkali, or liquor of flints. From this the silica is obtained in a pure state, by the addition of an acid. Glass, when melted and dropped into water, assumes an oval form, with a slender projection, called a tail. This is called Prince Rupert's drop. If a small part of this tail be broken off, the whole bursts into powder, with a kind of explosion. The Bologna, or philosophical phial, is a small cylindrical vessel of glass, rounded at the bottom, but open at the upper end. It is made thick at the bottom, so as not to be easily broken; but if a pebble be dropped into it, it immediately cracks, and the whole falls into pieces. In both these, (the drop and the bottle,) the glass is unannealed. When the external part of glass is suddenly cooled, the inner part is kept, as it were, contracted. Now annealing, the process of tempering glass in an oven, renders the glass uniformly alike, and capable of sustaining the variations of temperature, without breaking. By a crack or fissure, the internal parts which remained in a state of tension, endeavour to recover the full state of expansion, and consequently the glass is rent asunder. _Sec. XLVIII. Glue and Isinglass._ Both glue and isinglass are animal products. They are used in fire-works, but always in the state of solution, as vehicles to mix up compositions in order to make them unite, and to preserve them from falling to powder. The quantity, however, is never large, or either would destroy the effect. The proportions are generally prescribed. A solution of glue is employed in the old process for refining saltpetre. See _Nitre_. In making priming paste, isinglass dissolved in brandy is sometimes used.