The second bath of the two-bath chrome tannage consists of a solution of sodium thiosulphate acidified with hydrochloric acid. The reactions in this bath are somewhat complicated, several occurring simultaneously. Broadly speaking, the final result is due to (1) the reduction of the chromic acid to a chromic salt by the sulphurous acid; (2) the formation of a basic chromic salt owing to the excess of thiosulphate; (3) the reaction of the added acid and thiosulphate to give free sulphur, which is deposited in and on the leather. The relative intensity of these effects is variable, according to the conditions of operation, _e.g._ the amounts of chemicals used, their concentration, the nature and condition of the goods, the time of application, the manner of application, etc. In practice the most favourable conditions are usually discovered empirically, but, broadly speaking, the goods are usually added soon after the thiosulphate and acid are well mixed. There is some evidence that the reduction is in steps, intermediate products such as sodium tetrathionate and chromium dioxide are known to be formed. The goods change from yellow to dark brown, then to green, and finally to the familiar blue. The sulphur makes the final colour a lighter blue than in the case of a one-bath tannage, hence the two-bath process is often preferred for "colours." On account of the empirical character of this "hypo bath," it is impossible to fix any exact relation between the quantities of material used in the chroming bath, and the quantities of "hypo" and acid used in the reducing bath. The following rules, therefore, must be understood as rough approximations for practical use, and though they have been empirically discovered their theoretical significance is often fairly obvious. 1. The amount of hypo necessary is almost directly proportional to the amount of dichromate used. In chroming with baths of the acid or neutral type, the percentage of hypo should be about three times the percentage of dichromate used. Thus 4 per cent. dichromate needs 12 per cent. hypo; and 6 per cent. dichromate needs 18 per cent. hypo on the pelt weight. In baths of the Schultz type a less proportion of hypo may suffice, but the 10 per cent. hypo for 5 per cent. dichromate, recommended by the Schultz patent, is generally considered rather insufficient. 2. The proportion of hypo is increased somewhat for the heavier classes of goods, and may even reach 20 per cent. of the pelt weight. 3. An increase in the proportion of hypo is usual with an increase in the amount of free acid in an acid chroming bath. 4. The percentage of hydrochloric acid in the reducing bath is roughly half that of the hypo, but is the most variable factor. The quantity varies with the rate and mode of addition, the class of goods under treatment, and the composition of the chroming bath.