of gold glass; the whole mass is heated until both become soft, and is then blown and formed into sheet, which, on examination, will be found to consist mainly of white glass, with its surface thinly covered with the glass stained with oxide of gold, while the beautiful ruby colour, which the gold imparts to the glass, appears pure and distinct. If such glass as this be heated to too high a temperature, as when it is used in the manufacture of stained glass windows, the ruby colour is in part, and sometimes altogether, destroyed, for the oxide of gold loses its oxygen, and metallic gold is left behind, which does not yield a colour to the silicate. I have in my possession a piece of French glass of a pale sapphire tint, which, when heated in the oxidizing flame of the blowpipe, assumes a brilliant and intense ruby colour, showing that in the first condition, the gold is not in a state of oxidation sufficient to impart colour to the glass. When the suboxide of copper is mixed and fused with the glass which it is intended to colour, the result is an opaque substance, almost like red bottle-sealing-wax, which is treated in a manner exactly similar to the gold glass; viz. it is coated with white glass, and blown and shaped into sheets, which owe their intense ruby colour to a thin film of the coloured glass closely adhering to the mass of the white upon which it is placed. Glass made in this way is called "coated," and sometimes "flashed" glass, and is extremely useful for ornamental purposes, for by the action upon the coloured surface of hydrofluoric acid, the ruby coating can be eaten away, and the white glass beneath left entire. If the backgrounds of the patterns be painted upon the ruby side with a material like Brunswick black, which is able to resist the action of hydrofluoric acid, and if the plate of glass, on its ruby side, be exposed to the action of the vapour of this acid, or to the action of the acid in solution in water, in a short space of time the pattern will be eaten away; and if the Brunswick black coating be removed with turpentine, a sheet of ruby glass will be obtained with a white pattern etched upon it. Owing to the powerful colouring properties which oxide of cobalt exerts, a very deep-coloured blue glass can be made, which can be treated like the red copper glass, and may be made to coat and cover in the same way the surface of plates of white glass. Purple glass, coloured with oxide of manganese, and green glass are also sometimes used as coating materials for white glass, but other colours are never employed in this way.