When the matter is in fusion keep stirring it from time to time, that all the parts thereof may be equally acted on by the air and the fire. On the surface of the melted Iron _scoriæ_ will be formed, which must be taken off as they appear. At the same time you will see a great many sparkles darted up from the surface of the metal, which will form a sort of fiery shower. By degrees, as the Iron grows purer, the number of these sparkles diminishes, though they never vanish entirely. When but few sparkles appear, remove the coals which cover the Iron, and let the slag run out of the vessel; whereupon the metal will grow solid in a moment. Take it out while it is still red-hot, and give it a few strokes with a hammer, to try if it be ductile. If it be not yet malleable, repeat the operation a second time, in the same manner as before. Lastly, when it is thus sufficiently purified by the fire, work it for a long time on the anvil, extending it different ways, and making it red-hot as often as there is occasion. Iron thus brought to the necessary degree of ductility, so as to yield to the hammer, and suffer itself to be extended every way, either hot or cold, without breaking to bits, or even cracking in the least, is very good and very pure. If it cannot be brought to this degree by the method here prescribed, it is a proof that the ore from which this Iron was extracted ought to be mixed with other ores; but it frequently requires a great number of trials to obtain an exact knowledge of the quality and proportion of those other ores with which it is to be mixed. _OBSERVATIONS._ The brittleness and shortness of Pig-iron arises from the heterogeneous parts which it contains, and which could not be separated from it by the first fusion. These extraneous matters are usually Sulphur, Arsenic, and unmetallic earth, and also a ferruginous earth; but such as could not be combined with the phlogiston as it ought to be, in order to have the properties of a metal, and must therefore be considered as heterogeneous, with respect to the other well-conditioned martial particles. The Pig-iron, by undergoing repeated fusions, is freed from those heterogeneous matters; those which are volatile, such as Sulphur and Arsenic, being dissipated, and the unmetallic matters being scorified. As to the ferruginous earth, which did not at first acquire the metalline form, it becomes true Iron at last; because, among the coals with which it is encompassed, it meets with a sufficient quantity of phlogiston to reduce it to metal. Charcoal is also necessary on this occasion, that it may continually furnish phlogiston to the Iron, which would otherways be converted into a calx. Hammering the red-hot Iron, after each fusion, serves to force out from amongst the martial parts such earthy matters as may happen to remain there, and so bring into closer contact the metalline parts which were separated before by the interposition of those heterogeneous matters. PROCESS III.