4. Puzzolanic material is a valuable addition to cement for sea-water construction, 5. As little gypsum as possible should be added for regulating the time of setting to cements which are to be used in sea- water. 6. Sand containing a large proportion of fine grains must never be used in concrete or mortar for sea-water construction. 7. The proportions of the cement and aggregate for sea-water construction must be such as will produce a dense and impervious concrete. On the whole, sea-water has very little chemical effect on good Portland cements, such as are now easily obtainable, and, provided the proportion of aluminates is not too high, the varying composition of the several well-known commercial cements is of little moment. For this reason tests on blocks immersed in still salt water are of very little use in determining the probable behaviour of concrete when exposed to damage by physical and mechanical means, such as occurs in practical work. The destruction of concrete works on the sea coast is due to the alternate exposure to air and water, frost, and heat, and takes the form of cracking or scaling, the latter being the most usual when severe frosts are experienced. When concrete blocks are employed in the construction of works, they should be made as long as possible before they are required to be built in the structure, and allowed to harden in moist sand, or, if this is impracticable, the blocks should be kept in the air and thoroughly wetted each day. On placing cement or concrete blocks in sea water a white precipitate is formed on their surfaces, which shows that there is some slight chemical action, but if the mixture is dense this action is restricted to the outside, and does not harm the block. Cement mixed with sea water takes longer to harden than if mixed with fresh water, the time varying in proportion to the amount of salinity in the water. Sand and gravel from the beach, even though dry, have their surfaces covered with saline matters, which retard the setting of the cement, even when fresh water is used, as they become mixed with such water, and thus permeate the whole mass. If sea water and aggregate from the shore are used, care must be taken to see that no decaying seaweed or other organic matter is mixed with it, as every such piece will cause a weak place in the concrete. If loam, clay, or other earthy matters from the cliffs have fallen down on to the beach, the shingle must be washed before it is used in concrete.