The crude glass thus obtained is usually full of bubbles: it is as hard as common glass: it is of a blackish gray, and more or less transparent at the edges. Sometimes it has a whitish colour, and at others is yellowish or reddish, indicating thereby that the quantity of charcoal has been too small. Exposed to the air for several weeks, it undergoes slight changes, which tend rather to improve than injure its qualities. It attracts a little moisture from the air, which slowly penetrates its mass without changing its aggregation or appearance, except that it cracks, and a slight efflorescence appears at its surface. If after this it be exposed to heat, it swells up, owing to the escape of the moisture it has absorbed. In order to prepare the glass for solution in water it must be reduced to powder by stampers. One part of the glass requires from four to five of water for its solution. The water is first boiled in an open vessel, the powdered glass is added gradually, and is continually stirred, to prevent its adhesion to the vessel. The boiling must be continued for three or four hours, until no more glass is dissolved. If the boiling be checked before the liquor has thus attained the proper degree of concentration, carbonic acid will be absorbed by the potash from the air, and produce an injurious effect. When the solution has acquired the consistence of syrup, and a density of 1·24, it is fit for use. It is then allowed to repose, in order that the insoluble parts may be deposited: while it is cooling a film forms on the surface, which after some time disappears, or may be dissolved by depressing it in the liquor. Soluble glass being employed only in the liquid state, it is preserved for use in solution. No particular care is necessary to preserve the liquid, as, even after a long space of time, it undergoes no perceptible change, if the solution have been properly prepared. The only precaution is not to allow too free an access of air to it. Soluble glass may be prepared by using carbonate of soda, instead of that of potash. This glass has the same properties as the other, but is more valuable in its applications. The solutions of these two kinds of glass may be mixed in any proportion, and the mixture is sometimes more useful than either of the solutions separately. The solution of soluble glass is viscid, and when concentrated becomes turbid or opalescent. The solution unites with water in all proportions. At a density of 1·28 it contains nearly 28 per cent. of glass, and if the concentration be carried beyond this point, it becomes so viscid that it may be drawn out in threads like molten glass. When the solution is applied to other bodies, it dries rapidly in the air, and forms a coat like a varnish; a property which leads us to notice some of the numerous and varied applications of this curious preparation.