When the plate is ready, rest it upon the glass dipper, Collodion side uppermost, and lower it into the solution by a slow and steady movement: if any pause be made, a horizontal line corresponding to the surface of the liquid will be formed. Then place the cover upon the vertical trough[35] and darken the room, if this has not already been done. As the presence of white light does no injury to the plate previous to its immersion in the Bath, it is not necessary to exclude it during the time of coating with Collodion. [35] Troughs made of gutta-percha, glass, or porcelain are commonly used; the latter are the best, being quite opaque and not liable to cracks or leaking. When the plate has remained in the solution about twenty seconds, lift it partially out two or three times, in order to wash away the Ether from the surface. An immersion of one minute to a minute and a half will usually be sufficient; or two minutes in cold weather, and with Collodion containing but little Alcohol. Continue to move the plate until the liquid flows off in a uniform sheet, when the decomposition may be considered to be sufficiently perfect. The principal impediment in this part of the process lies in the difficulty with which Ether and Water mix together, which causes the Collodion surface on its first immersion to appear oily and covered with streaks. By gentle motion the Ether is washed away, and a smooth and homogeneous layer obtained. The plate is next removed from the dipper, and held vertically in the hand for a few seconds upon blotting paper, to drain off as much as possible of the solution of Nitrate of Silver.[36] It is then wiped on the back with filtering-paper, placed in a clean and dry slide, and is ready for the Camera. [36] This blotting-paper must be frequently changed, or stains will be produced at the lower edge of the plate during the development. The amateur is strongly recommended not to proceed to take pictures in the Camera until by a little practice he has succeeded in producing a perfect film which is uniform in every part and will bear inspection when washed and brought out to the light. It should, if properly prepared, present the following appearance:--Smooth and uniform, both by reflected and transmitted light; free from wavy lines or markings such as would be caused by a glutinous Pyroxyline, and from opaque dots due to small particles of dust or Iodide of Silver in suspension in the Collodion.