GOOD "MAKE" IN COLORED STONES. Brilliants, cut from materials having smaller refractive indices than diamond, (and this group includes nearly all stones other than diamonds) should have steeper back angles and higher tops than the best diamond brilliants have. A 35-degree top angle (the angle between the slope of the top and the plane of the girdle is called the top angle) and a 41-degree back angle being about ideal for diamond, other gem materials should have more nearly a 39-degree top angle and a 44-degree back angle to give the greatest possible brilliancy. However, in the case of colored gems such as ruby, sapphire, etc., where the value depends even more largely upon the color than upon the brilliancy, it is frequently necessary to cut the brilliant thicker or thinner than these proportions in order to deepen or to thin the color. In general, the thicker a stone of a given spread the deeper the color will be. The color may also be deepened by giving to the stone a rounded contour, both above and below the girdle, and facetting it in steps instead of in the brilliant form. Increasing the number of steps also serves to slightly deepen the color, as a larger number of reflections is thus obtained within the material, the light thus has to travel a greater distance through the colored mass, and more of the light, of color other than that of the stone, is absorbed. IMPROVING COLOR BY PROPER CUTTING. In addition to the color improvement that can be brought about by changing the shape of the cut stone there are a number of gem materials whose color varies very greatly in different directions, and this fact calls for skillful use in order to obtain the best possible results. Thus most tourmalines of deep color must be cut with the top or table, of the finished stone, on the _side_ of the prismatic crystal rather than at right angles to the axis of the prism. If cut the latter way they would be much too dense in color. On the other hand, most blue sapphires should be cut _across_ the prism axis rather than the way that tourmalines should be cut. To cut a sapphire with its table on the side of the prism would be likely to cause it to have a greenish cast because of the admixture of the unpleasing "ordinary ray" of yellowish tint with the blue of the stone as seen up and down the prism. Some Australian sapphires are of a pronounced green when viewed across the axis of the crystal. Rubies if cut, as was recommended for sapphires, give a very pure and very deep red color, but lack somewhat in the display of dichroism given by rubies that are cut with the table on the side of the crystal and parallel to its axis. Lapidaries need to know and to make use of such optical relations as these and jewelers might well inform themselves in such matters, especially if they have, or hope to acquire, trade in very fine colored stones.