After this, the last operation consists in firing the pieces a second time, to give them that neat and finished look which belongs to glazed substances. The saggers, ovens, and the mode of conducting the fire do not differ in this case from those used for making biscuit. The ovens are, however, smaller, and the saggers cannot be packed so closely with the different articles, as every piece has to be isolated, otherwise the glaze in melting would cause them to stick together. To provide against this, small implements made of clay cut in different forms are used, and, not to disfigure the ware, are contrived in such a way that the points of contact between them and the pieces should be as small as possible. This second firing does not take more than fifteen or eighteen hours, and this completes the series of operations, by which ordinary earthenware sold in the white or printed state may be produced. The reader must understand that the majority of these processes are also applicable to the manufacture of china, or any other glazed pottery, with some modifications which I shall take the opportunity of noticing, when speaking of these varieties. Pottery may be decorated in a great number of ways, and the operations are so varied that I cannot describe them all intelligibly, should I attempt to do so in my limited space. I shall consequently speak only of the paintings executed on the surface. This necessitates the use of colours specially prepared and made from two distinct materials; the bases and the fluxes. The bases are generally metallic oxides or highly oxidized compounds; the fluxes are vitreous substances, similar to the glazes, but softer, whose function is, to fix the colours permanently on the ware. When both, after being intimately ground together, are fired at a moderate heat on the article, the fluxes will cause the colour of the bases to look more vigorous and brighter, the effect being rather similar to that of an oil or transparent varnish on ordinary body colour. For this object, they must have very little chemical action, and be sufficiently soft to act in a moderate quantity. If, by carelessness or accident, the temperature is raised to a degree higher than the one exactly required, new compounds are formed, and the alteration of the colour is the consequence. There are some instances in which no fluxes are required; this is the case, when the ware has been coated with a glaze sufficiently fusible to allow the bases to sink in it, as soon as it begins to soften under the influence of heat. By this process more force and effect are obtained. It is, however, seldom used, for this reason, that from the care and attention which it requires in the superintendence of the firing, the manufacturer would run greater risks, and, being unable to use large ovens, would not turn out the same quantity of ware. Altogether it is a very expensive process.