When it is desired to apply to any portion of white glass some yellow silver stain, this can be done either in the first firing, by floating it on to the places to be stained, and allowing it to run in a sort of stream from the brush, so that it will evenly cover the surface and cause the heavier portions of the stain, namely, the mixed metallic silver and antimony, to sink regularly to the bottom, and come fairly in contact with the glass. Not very long ago, it was mentioned to me by a glass painter of note, that the workmen much prefer using the old stain made with silver and antimony, to that which is produced by using nitrate of silver. This really is a mistake on their part, for, when properly managed (and the knowledge of how to manage this stain can be acquired with very little trouble), the nitrate of silver stain is by far the best, and produces much better tints, with less chance of what the men call sulphuring when the glass is fired. This sulphuring is simply the result of opacity, obtained by heating the glass to too high a temperature. If the staining is to be performed in the same firing as that by which the painting is to be fixed, it is quite clear that the outlines of the part to be stained must be painted in, with tar-oil, or with some such substance which is not affected by the moisture of the stain. However, in general, the staining operation is performed after the first firing, that is to say, those pieces of glass to which the silver is to be applied are stained in the method above described after the first firing, and are then fired again, because the heat required to produce a good stain from silver is of a somewhat different character from that which is required simply to fuse the flux that binds the pigment to the glass. A longer and less intense heat, technically called a "soaking," is the best for producing an even and pure yellow tint. If the temperature be allowed to rise too high, the oxide of silver, which alone can stain the glass, gets reduced wholly or in part, and when this happens to only a slight extent, it destroys the transparency of the stain; and when it happens to a great extent, it destroys its colour altogether, making the glass opaque.