This scrap is taken and granulated in an iron rotary cutter mill, to a degree of fineness that will pass a 1/8″ mesh, it is then screened and mixed with a secret binder that has a wonderful holding quality; it is then dried by steam and pressed into sheets by hydraulic presses, dried again, and then stamped out in the usual manner. There is no waste to this process as the unused portions go back to the grinders again and through the usual process. Granulated cork is made by grinding the waste in ordinary metal roller, cage or bur mills, and then screening same for the various degrees of fineness; if cork-flour is desired, a tube mill may be used. These two uses are generally confined to the best scrap, but there still remains a large quantity which has a great value. A portion of this is made into Spanish black by carbonizing same in a closed iron kettle, or retort, and then grinding same in a regulation ball mill, until the desired fineness is obtained; this process producing a very fine black. The above uses in no degree exhaust the amount of scrap corkwood that leaves the various factories here and abroad, nor is its usefulness expended, for there is one use to which cork scrap is being put that bids fair to rival the stopper industry in importance, and that is in the form of cork-board for insulating purposes. The processes for the making of cork-board differ in many ways, widely divergent in principle. The corkwood waste and virgin cork are broken up and chipped in an ordinary iron mill as a preliminary to all processes; in one, claimed to be the best, this chipped material is poured into iron molds the desired shape of the slab, subjected to heavy pressure and run into an oven kept at about 800 to 900 degrees Fahrenheit. This oven, being a low brick type, resembling a lear and heated by coal fires, the slab molds being drawn through on an endless chain, which runs at a speed to keep the cork in just long enough, for the resin in same to exude and bind the little particles together; the cork is also charred in this process, thereby converting it into a carbonized cellulose which makes it an excellent material for insulation. Steam-heated hydraulic presses are also used for making small tile, etc., being the same principle as above, without the charring. The other process involves the use of tar, pitch or asphaltum, as a binder for the cork particles, and in one, the cork is mixed with a clay before being mixed with the asphaltum. The binder being heated in steam jacketed kettles, and in one it is mixed in the proportion of one to four, while in the other it is forced into the mass under pressure and then drawn out again by vacuum, both mixtures being poured into molds of the desired shape of the slab or in large molds, to be cut up after, and subjected to heavy pressure, the sawing being done by an ordinary rip-saw, cutting the block into any desired thickness of slab.