Great quantities of silver are used for making jewelry and for tableware. The one objection to its use is that silver likes to unite with sulphur, and thus the silver easily becomes black. There is sulphur in the yolk of an egg and that is why the spoon with which it has been eaten turns black. Even if silverware is not used, it tarnishes, especially in towns, because there is so much sulphureted hydrogen in the air. In perfectly pure air, it would not tarnish. Silver is harder than gold, but not hard enough to be used without some alloy, usually copper. Tableware is "solid" even if it contains alloy enough to stiffen it. It is "plated" if it is made of some cheaper metal and covered with silver. The old way of doing this was to fasten with bits of solder a thin sheet of silver to the cup or vase or whatever was in hand and heat it. This did fairly well for large, smooth articles; but it was almost impossible to finish the edges of spoons so as not to show the two metals. If you look at a plated spoon to-day, however, you will find that there is no break at the edge, and so far as you can tell by the eye, it is solid silver. If you look on the back of the spoon, you will perhaps see "Rogers Bros. 1846." These men were the first silvermakers in this country to plate tableware by electricity. To make a spoon, they formed one out of iron or copper and made sure that it was perfectly clean. Then across a bath of silver cyanide, potassium cyanide, and water they laid two metal rods, and from these they hung a spoon at one end and a plate of silver at the other. These rods were connected with the two poles of a battery. The electrical current passed through them, released the silver from the silver cyanide, and this was deposited upon the spoon. The cyanide that had lost its silver took enough more from the silver plate to make up. The amount of silver on the spoon depends upon the length of time it remains in the bath. It is weighed before plating and again afterwards, to make sure that the proper amount of silver has been deposited upon it. On the back of many plated articles you will see the words "Triple plate" or "Quadruple plate." If the article has been made by a reliable firm, this means that the triple plate it manufactures contains three times as much silver as "single plate," and that quadruple plate contains four times as much. A piece of silver looks just as well if it has stayed in the bath only a few minutes, but of course it has taken on so little silver that this will soon wear off and show the cheaper metal.