The operation of the cupel is chiefly used to purify Silver from the alloy of Copper; because this metal, being more fixed and harder to calcine than other metallic substances, is the only one that remains united with Silver and Lead, after roasting and scorification with Lead. It requires no less than sixteen parts of the Lead to destroy it in the cupel, and separate it from Silver. It melts into one mass with the Lead; and the glass produced by these two metals, deprived of their phlogiston, inclines to a brown or a black colour; by which appearance chiefly we know that our Silver was alloyed with Copper. PROCESS III. _To purify Silver by Nitre._ Granulate the Silver you intend to purify, or reduce it to thin plates; put it into a good crucible; add thereto a fourth part in weight of very dry pulverized Nitre, mixed with half the weight of the Nitre of calcined Wine-lees, and about a sixth part of the same weight of common glass in powder. Cover this crucible with another crucible inverted; which must be of such a size that its mouth may enter a little way into that of the lower one, and have its bottom pierced with a hole of about two lines in diameter. Lute the two crucibles together with clay and Windsor-loam. When the lute is dry, place the crucibles in a melting furnace. Fill the furnace with charcoal, taking care however that the fuel do not rise above the upper crucible. Kindle the fire, and make your vessels of a middling-red heat. When they are so, take up with the tongs a live-coal, and hold it over the hole of the upper crucible. If you immediately perceive a vivid splendour round the coal, and at the same time hear a gentle hissing noise, it is a sign that the fire is of a proper strength; and it must be kept up at the same degree till this phenomenon cease. Then increase the fire to the degree requisite to keep pure Silver in fusion; and immediately after take your vessels out of the furnace. You will find the Silver at the bottom of the lower crucible, covered with a mass of Alkaline scoria of a greenish colour. If the metal be not rendered perfectly pure and ductile by this operation, it must be repeated a second time. _OBSERVATIONS._