It is of great importance to keep the temperature of the upper part of the furnace steadily at a red heat and flaming, as the colour of the sublimate will be inferior if the temperature is either too high or too low. To facilitate the proper regulation of the temperature, a pyrometer (which may be similar to the kind used in ironworks) is employed, which pyrometer is placed in the flue at a distance from the furnace where it cannot be injured; and by a few trials is ascertained what temperature should be indicated by the pyrometer when the temperature in the furnace is what it should be. This point having been ascertained, a glance at the pyrometer will at any time show whether the furnace is working properly or not. The inventors also provide for rapidly cooling the upper part of the furnace without interfering with the lower part, in the event of the heat becoming too great, by arranging a water pipe _w_, with a set of jets, round the top of the furnace, so that on turning a tap on the supply pipe a spray of water may be applied to the outside of the furnace; and as it is desirable that water applied in this way should not run down to the lower part of the furnace they build gutter plates _x_ into the sides of the furnace just above the charging door _f_, to lead off any surplus water to a drain pipe. Sufficient hydrochloric acid may be formed or introduced, as hereinbefore described, not only for forming chloro-sulphite of lead in the condenser, but also for saturating all the free oxide of lead, and for combining with and rendering soluble any iron, zinc, antimony, silver, or other metals. The chlorides thus formed become dissolved in the water of the condenser, and the solution, separated from the insoluble white pigment, may be treated by known processes for recovery of the metals. When the lead ores or other lead-yielding materials contain silver to a greater extent than 5 oz. per ton, a notable quantity of the silver is volatilised, and if it is left in the white pigment it renders the latter sensitive to sunlight; whereas if rendered soluble in the manner hereinbefore described, and separated by any of the known processes, it becomes a source of profit. The white pigment is washed in the ordinary way; and when chloride of zinc is not completely removed by washing, a small quantity of sulphuric acid may be mixed with the pigment, by adding the same to the last washing water, to convert the chloride of zinc into sulphate, which is not hygroscopic. The white pigment made as hereinbefore described is a very good and economical material for manufacturing into chrome yellow, this being done by mixing a solution of any suitable chromate or bichromate with the wet pigment; whilst the chrome yellow thus obtained may be converted into chrome orange or red by treating it in the usual way.