_The form of an 'ash'_ derived from a fibrous structure, is that of the 'organic' original, more or less, according to its proportion and composition. The proportion of 'natural ash' is seldom large enough, nor are the components of such character as to give a coherent ash, but if in the case of a fibrous structure it is combined or intimately mixed with inorganic compounds deposited within the fibres from solution, the latter may be made to yield a perfect skeleton of the fibre after burning off the organic matter. It is by such means that the mantles used in the Welsbach system of incandescent lighting are prepared. A purified cotton fabric--or yarn--is treated with a concentrated solution of the mixed nitrates of thorium and cerium, and, after drying, the cellulose is burned away. A perfect and coherent skeleton of the fabric is obtained, composed of the mixed oxides. Such mantles have fulfilled the requirements of the industry up to the present time, but later experiments forecast a notable improvement. It has been found that artificial cellulose fibres can be spun with solutions containing considerable proportions of soluble compounds of these oxides. Such fibres, when knitted into mantles and ignited, yield an inorganic skeleton of the oxides of homogeneous structure and smooth contour. De Mare in 1894, and Knofler in 1895, patented methods of preparing such cellulose threads containing the salts of thorium and cerium, by spinning a collodion containing the latter in solution. When finally ignited, after being brought into the suitable mantle form, there results a structure which proves vastly more durable than the original Welsbach mantle. The cause of the superiority is thus set forth by V. H. Lewes in a recent publication (J. Soc. of Arts, 1900, p. 858): 'The alteration in physical structure has a most extraordinary effect upon the light-giving life of the mantle, and also on its strength, as after burning for a few hundred hours the constant bombardment of the mantle by dust particles drawn up by the rush of air in the chimney causes the formation of silicates on the surface of the mantle owing to silica being present in the air, and this seems to affect the Welsbach structure far more than it does the "Clamond" type, with the result that when burned continuously the Welsbach mantle falls to so low a pitch of light emissivity after 500 to 600 hours, as to be a mere shadow of its former self, giving not more than one-third of its original light, whilst the Knofler mantle keeps up its light-emitting power to a much greater extent, and the Lehner fabric is the most remarkable of all. Two Lehner mantles which have now been burning continuously in my laboratory for over 3,000 hours give at this moment a brighter light emissivity than most of the Welsbachs do in their prime.' ...'The new developments of the Clamond process form as important a step in the history of incandescent gas lighting as the discoveries which gave rise to the