This cinder now plays a very important part in the process. It takes up the oxides of iron formed by the contact of the oxidizing flame with the exposed portion of the metal bath, and at the same time the carbon of the iron, coming in contact with the under surface of the cinder covering, where it is protected from oxidizing influences, reduces these oxides from the cinder and restores them to the bath in metallic form. This alternate oxidation of exposed metal, and its reduction by the carbon of the cast iron, continues till the carbon is nearly exhausted, when the iron assumes a pasty condition, or "comes to nature," as the puddlers call this change. The charge is then worked up into balls, and removed for treatment in the squeezer, and then hammered or rolled. In the Wilson process the conditions which we have noted in the puddling operation are very closely approximated. Iron ore reduced to a coarse sand is mixed with the proper proportion of charcoal or coke dust, and the mixture fed into upright retorts placed in the chimney of the puddling furnace. By exposure for 24 hours to the heat of the waste gases from the furnace, in the presence of solid carbon, a considerable portion of the oxygen of the ore is removed, but little or no metallic iron is formed. The ore is then drawn from the deoxidizer into the rear or second hearth of the puddling furnace, situated below it, where it is exposed for 20 minutes to a much higher temperature than that of the deoxidizer. Here the presence of the solid carbon, mixed with the ore, prevents any oxidizing action, and the temperature of the mass is raised to a point at which the cinder begins to form. Then the charge is carried forward by the workmen to the front hearth, in which the temperature of a puddling furnace prevails. Here the cinder melts, and at the same time the solid carbon reacts on the oxygen remaining combined with the ore, and forms metallic iron; but by this time the molten cinder is present to prevent undue oxidation of the metal formed, and solid carbon is still present in the mixture to play the same role, of reducing protoxide of iron from the cinder, as the carbon of the cast iron does in the ordinary puddling process. I have said that the cast iron used as the material for puddling contains about 3 per cent. of carbon; but in this process sufficient carbon is added to effect the reduction of the ore to a metallic state, and leave enough in the mass to play the part of the carbon of the cast iron when the metallic stage has been reached.