It is well known that the efficient preservation of iron against rusting is at present only provided for in cases where human life would be endangered by failure, as in the case of railway bridges and steamers. Thus, for example, at Mr. Cramer-Klett's ironworks at Nuremberg every piece of iron used for his bowstring bridges is dipped in oil heated to eight hundred degrees. The very great care which is at present taken in this matter may be judged from the current practice of most bridge and roofing manufacturers. Every piece of iron before being riveted in its place is cleaned from rust by being immersed in a solution of hydrochloric acid. The last traces of free acid having been cleared away, at first by quicklime and afterward by a copious ablution with hot water, the piece is immediately immersed in hot linseed oil, which protects every part of the surface from the action of the atmosphere. Afterward it is riveted and painted. Notwithstanding all this, the painting requires continual and careful renewal. On the Britannia Bridge, near Bangor, the painter is permanently at work; yet, in spite of all this care and expense, rust cannot be entirely avoided. The age of iron railway bridges is still too short to enable us to draw conclusions as to the probabilities of accidents. Now, Professor Barff has discovered a process by which iron may be kept from rusting by being entirely coated with its own sesquioxide. A piece of iron exposed to the action of superheated steam, in a close chamber and under a certain pressure, becomes gradually covered by a skin of this black oxide, of a thickness depending upon the temperature of the steam and the duration of the experiment. For instance, exposure during five hours to steam superheated to five hundred degrees will produce a hermetical coating capable of resisting for a considerable time the application of emery paper and of preserving the iron from rust even in a humid atmosphere, if under shelter from the weather. If the temperature is raised to 1,200 degrees, and the time of exposure to six or seven hours, the skin of sesquioxide will resist every mechanical action, and the influence of any kind of weather. The sesquioxide being harder than the iron itself, and adhering to its surface even more firmly than the atoms of iron do to each other, there is an increased resistance not only to chemical but also to mechanical action. The surface is not altered by the process in any other respect, a plain forging retaining its roughness, a polished piece its smooth surface. If the skin is broken away oxidation takes place, but only just on the spot from which the oxide has been removed. If Professor Barff's experiments are borne out by practice, this invention may become of very great importance. It is within the bounds of probability that it may enable iron, by increasing its facility in competing with wood, to recover, at least for a considerable time, even more than the ground it has