In heat-treating the forgings were laid on a rack or loop _A_, Fig. 14, made of 1-1/4-in. double extra-heavy pipe, bent up with parallel sides about 9 in. apart, one end being bent straight across and the other end being bent upward so as to afford an easy grasp for the hook. Fifteen rods were laid on each loop, there being four loops of rods charged into a furnace with a hearth area of 36 by 66 in. The rods were charged at a temperature of approximately 900 deg.F. They were heated for refining over a period of 3 hr. to 1,625 deg.F., soaked 15 min, at this degree of heat and quenched in soluble quenching oil. In pulling the heat to quench the rods, the furnace door was raised and the operator pulls one of the loops _A_, Fig. 15 forward to the shelf of the furnace, supporting the straight end of the loop by means of the porter bar _B_. They swung the loop of rods around from the furnace shelf and set the straight end of the loop on the edge of the quenching tank, then raise the curved end _C_, by means of their hook _D_ so that all the rods on the loop slide into the oil bath. Before the rods cooled entirely, the baskets in the quenching tank were raised and the oil allowed to partly drain off the forgings, and they were stacked on curved-end loops or racks and charged into the furnace for the second or hardening heat. The temperature of the furnace was raised in 1-1/2 hr. to 1,550 deg.F., the rods soaked for 15 min. at this degree of heat and quenched in the same manner as above. They were again drained while yet warm, placed on loops and charged into the furnace for the third or tempering heat. The temperature of the furnace was brought to 1,100 deg.F. in 1 hr., and the rods soaked at this degree of heat for 1 hr. They were then removed from the furnace the same as for quenching, but were dumped onto steel platforms instead of into the quenching oil, and allowed to cool on these steel platforms down to the room temperature. PICKLING THE FORGINGS The forgings were then pickled in a hot solution of either niter cake or sulphuric acid and water at a temperature of 170 deg.F., and using a solution of about 25 per cent. The solution was maintained at a constant point by taking hydrometer readings two or three times a day, maintaining a reading of about 1.175. Sixty forked or one hundred single rods were placed in wooden racks and immersed in a lead-lined vat 30 by 30 by 5 ft. long. The rack was lowered or lifted by means of an air hoist and the rods were allowed to stay in solution from 1/2 to 1 hr., depending on the amount of scale. The rods were then swung and lowered in the rack into running hot water until all trace of the acid was removed. The rod was finally subjected to Brinell test. This shows whether or not the rod has been heat-treated to the proper hardness. If the rods did not read between 241 and 277, they were re-treated until the proper hardness is obtained. CHAPTER IV