The advantage of direct quenching from the carbonizing heat is doubtless one of economy, and in many cases will save the cost of a reheating. Specifications for case hardening, issued by the Society of Automotive Engineers, have lately been revised; whereas they formerly called for a slow cooling, they now permit a quenching from the pot. Doubtless this is a step in advance. Warpage caused by quenching can be reduced to a minimum by thoroughly annealing the stock before any machine work is done on it. Another advantage obtained from rapid cooling from the carbonizing heat is the retaining of the majority of the excess cementite in solution which produces a less brittle case and by so doing reduces the liability of grinding checks and chipping of the case in actual service. In the case of the camshaft, it is not possible to quench directly from the carbonizing heat because of distortion and therefore excessive breakage during straightening operations. All Liberty camshafts were cooled slowly from carbonizing heat and hardened by a single reheating to a temperature of from 1,380 to 1,430 deg.F. and quenching in water. Considerable trouble has always been experienced in obtaining uniform hardness on finished camshafts. This is caused by insufficient water circulation in the quenching tank, which allows the formation of steam pockets to take place, or by decarbonization of the case during heating by the use of an overoxidizing flame. Another cause, which is very often overlooked, is due to the case being ground off one side of cam more than the other and is caused by the roughing master cam being slightly different from the finishing master cam. Great care should be taken to see that this condition does not occur, especially when the depth of case is between 1/32 and 3/64 in. CARBON-STEEL FORGINGS Low-stressed, carbon-steel forgings include such parts as carbureter control levers, etc. The important criterion for parts of this type is ease of fabrication and freedom from over-heated and burned forgings. The material used for such parts was S. A. E. No. 1,030 steel, which is of the following chemical composition: Carbon, 0.250 to 0.350 per cent; manganese, 0.500 to 0.800 per cent; phosphorus, 0.045 maximum per cent; sulphur, 0.050 maximum per cent. To obtain good machineability, all forgings produced from this steel were heated to a temperature of from 1,575 to 1,625 deg.F. to refine the grain of the steel thoroughly and quenched in water and then tempered to obtain proper machineability by heating to a temperature of from 1,000 to 1,100 deg.F. and cooled slowly or quenched.