My first 15 inch speculum was an alloy of copper and tin, in the proportions given by Lord Rosse. His general directions were closely followed, and the casting was very fine, free from pores, and of silvery whiteness. It was 2 inches thick, weighed 110 pounds, and was intended to be of 12 feet focal length. The grinding and polishing were conducted with the Rosse machine. Although a great amount of time was spent in various trials, extending over more than a year, a fine figure was never obtained--the principal obstacle to success being a tendency to polish in rings of different focal length. It must, however, be borne in mind that Lord Rosse had so thoroughly mastered the peculiarities of his machine as to produce with it the largest specula ever made and of very fine figure. During these experiments there was occasion to grind out some imperfections, 8/100 of an inch deep, from the face of the metal. This operation was greatly assisted by stopping up the defects with a thick alcoholic solution of Canada balsam, and having made a rim of wax around the edge of the mirror, pouring on nitro-hydrochloric acid, which quickly corroded away the uncovered spaces. Subsequently an increase in focal length of 15 inches was accomplished, by attacking the edge zones of the surface with the acid in graduated depths. An attempt also was made to assist the tedious grinding operation by including the grinder and mirror in a Voltaic circuit, making the speculum the positive pole. By decomposing acidulated water between it and the grinder, and thereby oxidizing the tin and copper of the speculum, the operation was much facilitated, but the battery surface required was too great for common use. If a sufficient intensity was given to the current, speculum metal was transferred without oxidation to the grinder, and deposited in thin layers upon it. It was proposed at one time to make use of this fact, and coat a mirror of brass with a layer of speculum metal by electrotyping. The gain in lightness would be considerable. During the winter of 1860 the speculum was split into two pieces, by the expansion in freezing of a few drops of water that had found their way into the supporting case. (2.) Silvering Glass. At Sir John Herschel’s suggestion (given on the occasion of a visit that my father paid him in 1860), experiments were next commenced with silvered glass specula. These were described as possessing great capabilities for astronomical purposes. They reflect more than 90 per cent. of the light that fulls upon them, and only weigh one-eighth as much as specula of metal of equal aperture. As no details of Steinheil’s or Foucault’s processes for silvering in the cold way were accessible at the time, trials extending at intervals over four months were made. A variety of reducing agents were used, and eventually good results obtained with milk sugar.