Generally silvered mirrors are very enduring, and will bear polishing repeatedly, if previously dried by heat. I have some which have been used as diagonal reflectors in the Newtonian, and have been exposed during a large part of the day to the heat of the sun concentrated by the 15-1/2 inch mirror. These small mirrors are never covered, and yet the one now in the telescope has been there a year, and has had the dusty film--like that which accumulates on glass--polished off it a dozen times. In order to guard against tarnishing, experiments were at first made in gilding silver films, but were abandoned when found to be unnecessary. A partial conversion of the silver film into a golden one, when it will resist sulphuretted hydrogen, can be accomplished as follows: Take three grains of hyposulphite of soda, and dissolve it in an ounce of water. Add to it slowly a solution in water of one grain of chloride of gold. A lemon yellow liquid results, which eventually becomes clear. Immerse the silvered glass in it for twenty-four hours. An exchange will take place, and the film become yellowish. I have a piece of glass prepared in this way which remains unhurt in a box, where other pieces of plain silvered glass have changed some to yellow, some to blue, from exposure to coal gas. I have also used silvered glass plates for daguerreotyping. They iodize beautifully if freshly polished, and owing probably to the absence of the usual copper alloy of silver plating, take impressions with very short exposures. The resulting picture has a rosy warmth, rarely seen in ordinary daguerreotypes. The only precaution necessary is in fixing to use an alcoholic solution of cyanide of potassium, instead of hyposulphite of soda dissolved in water. The latter has a tendency to split up the silver. The subsequent washing must be with diluted common alcohol. Pictures obtained by this method will bear high magnifying powers without showing granulation. Unfortunately the exposure required for them in the telescope is six times as great as for a sensitive wet collodion, though the iodizing be carried to a lemon yellow, the bromizing to a rose red, and the plate be returned to the iodine. (3.) GRINDING AND POLISHING GLASS. Some of the facts stated in the following paragraphs, the result of numerous experiments, may not be new to practical opticians. I have had, however, to polish with my own hands more than a hundred mirrors of various sizes, from 19 inches to 1/4 of an inch in diameter, and to experience very frequent failures for three years, before succeeding in producing large surfaces with certainty and quickly. It is well nigh impossible to obtain from opticians the practical minutiæ which are essential, and which they conceal even from each other. The long continued researches of Lord Rosse, Mr. Lassell, and M. Foucault are full of the most valuable facts, and have been of continual use.