The colouring matter in the European enamels may amount to as much as a third part of the total amount of the flux with which they are incorporated. As there is not enough of this flux to dissolve the whole of the oxides, the enamel remains dull and opaque after firing. The flux, in fact, is only used as a vehicle to attach the colour to the surface of the porcelain. The effect in consequence is inferior in brilliancy to that obtained by the Chinese with their transparent enamels in which the metallic oxides, present in much smaller quantity, are thoroughly dissolved to form a glass. There is, unfortunately, a practical obstacle to the application of these glassy enamels to the hard pastes and glazes of Europe. It is impossible to ensure their firm adhesion to the subjacent glaze. The Chinese, however, do not appear to find any difficulty in effecting this. The following explanation has been given to account for the difference of behaviour:--the tendency of the enamel to split off in cooling, as has been proved by experiment, arises from the small amount of contraction at that time of the highly kaolinic paste, compared with that of the superimposed glassy enamel. The more silicious paste used by the Chinese contracts, on the contrary, at the same rate approximately as the enamels that it carries, and these enamels may therefore be laid on in sufficient thickness without any risk of their subsequently splitting off.[22] To appreciate the difference in the decorative value of these two classes of enamels it is only necessary to compare the brilliant effect, say, of a piece of Chinese egg-shell of the time of Kien-lung with the tame surface of a contemporary Meissen plate, elaborately painted with landscapes or flowers. The glassy enamels used by the Chinese resemble the pastes used for artificial jewellery. They are essentially silicates of lead and an alkali. The composition of the flux has to be modified to ensure the full development of the colour of the different metallic oxides which are either made up with it or added subsequently. But in a general way we may say that the colourless fluxes which form the basis of the coloured enamels are prepared by melting in a crucible a mixture of pure quartz sand and red lead, and adding more or less alkali. In certain cases the lead predominates, as when it is proposed to make an emerald green enamel by means of copper, or when the flux is to serve as a basis for the ruby colour given by a minute quantity of gold. On the other hand, if copper be added to a flux containing an excess of either soda or potash, we obtain a turquoise blue. A fine purple, again, can only be obtained from manganese with an alkaline flux; if too much lead is present only a brown tint is obtainable.