When wrought iron is nearly pure, it has, when in bars of not less than an inch square, or plates not less than half an inch in thickness, a granular structure. From the appearance of these grains, an estimate may be had of its quality; grains without any determinate form, neither presenting, when broken, crystalline faces, nor arranging themselves in plates; and which, in the fracture of the bar, exhibit points, and even filaments, manifesting the resistance they have opposed, are marks of the best quality. If, when broken, a crystalline character is exhibited, the quality is bad, and will, according to a disposition difficult to describe in words, either break under the hammer when heated, or be subject to rupture when cold. These two opposite defects are, in the language of our manufacturers, called red and cold short, or shear. The former fault unfits it for being easily worked; the latter destroys its most important usefulness. When the manufacture has been badly conducted, crystals will appear mingled with tenacious grains, and a want of uniform consistence will render it unfit for being cut and worked by the file. Iron of the latter character may, notwithstanding, possess great tenacity. In still smaller bars, good iron, in breaking, exhibits filaments like those shown by a piece of green wood when broken across; this is technically called nerve; and as it does not show itself in larger bars, it has been supposed that it is the result of the process of drawing out the bars. This is partially true, although the iron that presents a crystalline structure will not acquire nerve, however frequently hammered. To obtain nerve in larger masses, it is necessary to form them of bundles of smaller bars, a process known under the name of faggoting. * * * * * Iron contains in its ores many impurities of different natures, according to circumstances, and is in its preparation exposed to several others; by these its quality is frequently much affected. Its valuable ores all contain the iron in the state of oxide. The oxygen, it is generally believed, is not wholly separated even in the best malleable iron, but enough still remains to impair in some degree its good qualities. In its manufacture it is exposed to the action of carbon, with which it is capable of combining. Much iron appears to contain some of the combinations of this sort, existing in the form of hard particles, technically known by the name of _pins_.