_Iron compounds_ are highly important because they exercise a powerful influence on the colour of the burned clays. The red oxide (ferric oxide) is the most useful form in burned clay, but in the raw material ferrous oxide and ferrous carbonate may also occur, though they are converted into the red oxide on heating. The red iron oxide, which is closely related to 'iron rust,' occurs in so finely divided a state that its particles appear to be almost as small as those of the finest clays. Hence attempts to improve the colour of terra-cotta and bricks by the addition of commercial 'iron oxide' are seldom satisfactory, the finest material obtainable being far coarser than that occurring in clays. It is a curious fact that red iron oxide does not appear to form any compound with the other constituents of clay under ordinary conditions of firing, and although a 'base' and capable of reducing the heat-resisting power of clays, it does not appear to do so as long as the conditions in the kiln are sufficiently oxidizing. It is this which enables red bricks and other articles to be obtained with remarkable uniformity of colour combined with great physical strength. In a reducing atmosphere, on the contrary, ferrous oxide readily forms and attacks the clay, forming a dark grey vitreous mass. If the iron particles are separated from each other they will, on reduction, form small slag-like spots, but if they are in an extremely fine state of division and well distributed, the brick or other article will become slightly glossy and of an uniform black-grey tint. The famous Staffordshire 'blue' bricks owe their colour to this characteristic; they are not really 'blue' in colour. The effect of chalk on the colour of red-burning clays has already been mentioned.