In making steel in the old way the cast iron was melted and the carbon and other impurities burned out of it, the melted iron being stirred or "puddled," meanwhile. The resulting puddled iron, also known as wrought iron, is very low in carbon; it is tough, and on being broken appears to be made up of a bundle of long fibers. Then the iron was heated to redness for several days in material containing carbon (charcoal) until it absorbed the desired amount, which made it steel, just as case-hardening iron or steel adds carbon to the outer surface of the metal. The carbon absorbed by the iron does not take on a graphitic form, however, as in the case of cast iron, but enters into a chemical compound with the iron, a hard brittle substance called "cementite" by metallurgists. In fact, the difference between the hard, brittle cementite and the soft, greasy graphite, accounts for many of the differences between steel and gray cast iron. Wrought iron, which has very little carbon of any sort in it, is fairly soft and tough. The properties of wrought iron are the properties of pure iron. As more and more carbon is introduced into the iron, it combines with the iron and distributes itself throughout the metal in extremely small crystals of cementite, and this brittle, hard substance lends more and more hardness and strength to the steel, at the expense of the original toughness of the iron. As more and more carbon is contained in the alloy--for steel is a true alloy--it begins to appear as graphite, and its properties counteract the remaining brittle cementite. Eventually, in gray cast iron, we have properties which would be expected of wrought iron, whose tough metallic texture was shot through with flakes of slippery, weak graphite. But to return to the methods of making steel tools in use 100 years ago. The iron bars, after heating in charcoal, were broken and the carbon content judged by the fracture. Those which had been in the hottest part of the furnace would have the deepest "case" and highest carbon. So when the steel was graded, and separated into different piles, a few bars of like kind were broken into short lengths, melted in fire-clay crucibles at an intense white heat, cast carefully into iron molds, and the resulting ingot forged into bars under a crude trip hammer. This melting practice is still in use for crucible steel, and will be described further on page 4. THE WORKING OF STEEL ANNEALING, HEAT TREATING AND HARDENING OF CARBON AND ALLOY STEEL CHAPTER I STEEL MAKING There are four processes now used for the manufacture of steel. These are: The Bessemer, Open Hearth, Crucible and Electric Furnace Methods. BESSEMER PROCESS The bessemer process consists of charging molten pig iron into a huge, brick-lined pot called the bessemer converter, and then in blowing a current of air through holes in the bottom of the vessel into the liquid metal.