The purpose for which this steel is annealed is a deciding factor as to what heat to give it. If it is for machineability only, the steel requires to be brought up slowly to just below the critical and then slowly cooled in the furnace or ash pit. It must be thoroughly covered so that there will be no access of cool air. If the annealing is to increase ductility to the maximum extent it should be slowly heated to slightly over the upper critical temperature and kept at this heat for a length of time necessary for a thorough penetration to the core, after which it can be cooled to about 1,200 deg.F., then reheated to about 1,360 deg.F., when it can be removed and put in an ash pit or covered with lime. If the annealing is just to relieve strains, slow heating is not necessary, but the steel must be brought up to a temperature not much less than a forging or rolling heat and gradually cooled. Covering in this case is only necessary in steel of a carbon content of more than 40 points. ANNEALING IN BONE Steel and cast iron may both be annealed in granulated bone. Pack the work the same as for case-hardening except that it is not necessary to keep the pieces away from each other. Pack with bone that has been used until it is nearly white. Heat as hot as necessary for the steel and let the furnace cool down. If the boxes are removed from furnace while still warm, cover boxes and all in warm ashes or sand, air slaked lime or old, burned bone to retain heat as long as possible. Do not remove work from boxes until cold. ANNEALING OF RIFLE COMPONENTS AT SPRINGFIELD ARMORY In general, all forgings of the components of the arms manufactured at the Armory and all forgings for other ordnance establishments are packed in charcoal, lime or suitable material and annealed before being transferred from the forge shop. Except in special cases, all annealing will be done in annealing pots of appropriate size. One fire end of a thermo-couple is inserted in the center of the annealing pot nearest the middle of the furnace and another in the furnace outside of but near the annealing pots. The temperatures used in annealing carbon steel components of the various classes used at the Armory vary from 800 deg.C. To 880 deg.C. or 1,475 to 1,615 deg.F. The fuel is shut off from the annealing furnace gradually as the temperature of the pot approaches the prescribed annealing temperature so as to prevent heating beyond that temperature. The forgings of the rifle barrel and the pistol barrel are exceptions to the above general rule. These forgings will be packed in lime and allowed to cool slowly from the residual heat after forging. CHAPTER VII CASE-HARDENING OR SURFACE-CARBURIZING