Carburizing, commonly called case-hardening, is the art of producing a high-carbon surface, or case, upon a low carbon steel article. Wrenches, locomotive link motions, gun mechanisms, balls and ball races, automobile gears and many other devices are thereby given a high-carbon _case_ capable of assuming extreme hardness, while the interior body of metal, the _core_, remains soft and tough. The simplest method is to heat the piece to be hardened to a bright red, dip it in cyanide of potassium (or cover it by sprinkling the cyanide over it), keep it hot until the melted cyanide covers it thoroughly, and quench in water. Carbon and nitrogen enter the outer skin of the steel and harden this skin but leave the center soft. The hard surface or "case" varies in thickness according to the size of the piece, the materials used and the length of time which the piece remains at the carburizing temperature. Cyanide case-hardening is used only where a light or thin skin is sufficient. It gives a thickness of about 0.002 in. In some cases of cyanide carburizing, the piece is heated in cyanide to the desired temperature and then quenched. For a thicker case the steel is packed in carbon materials of various kinds such as burnt leather scraps, charcoal, granulated bone or some of the many carbonizing compounds. Machined or forged steel parts are packed with case-hardening material in metal boxes and subjected to a red heat. Under such conditions, carbon is absorbed by the steel surfaces, and a carburized case is produced capable of responding to ordinary hardening and tempering operations, the core meanwhile retaining its original softness and toughness. Such case-hardened parts are stronger, cheaper, and more serviceable than similar parts made of tool steel. The tough core resists breakage by shock. The hardened case resists wear from friction. The low cost of material, the ease of manufacture, and the lessened breakage in quenching all serve to promote cheap production. For successful carburizing, the following points should be carefully observed: The utmost care should be used in the selection of pots for carburizing; they should be as free as possible from both scaling and warping. These two requirements eliminate the cast iron pot, although many are used, thus leaving us to select from malleable castings, wrought iron, cast steel, and special alloys, such as nichrome or silchrome. If first cost is not important, it will prove cheaper in the end to use pots of some special alloy. [Illustrations: FIGS. 27 to 30.--Case-hardening or carburizing boxes.] [Illustration: FIG. 31.--A lid that is easily luted.]