_The normal sulphocarbonate (viscose)._--In the industrial applications of viscose it is important to maintain a certain standard of composition as of the essential physical properties of the solution, notably viscosity. It may be noted first that, with the above-mentioned exception, the various fibrous celluloses show but slight differences in regard to all the essential features of the reactions involved. In the mercerising reaction, or alkali-cellulose stage, it is true the differences are considerable. With celluloses of the wood and straw classes there is a considerable conversion into soluble alkali-celluloses. If treated with water these are dissolved, and on weighing back the cellulose, after thorough washing, treatment with acid, and finally washing and drying, it will be found to have lost from 15 to 20 p.ct. in weight. The lower grade of celluloses thus dissolved are only in part precipitated in acidifying the alkaline solution. On the other hand, after conversion into viscose, the cellulose when regenerated re-aggregates a large proportion of these lower grade celluloses, and the final loss is as stated above, from 5 to 7 p.ct. only. Secondly, it is found that all the conditions obtaining in the alkali-cellulose stage affect the subsequent viscose reaction and the properties of the final solution. The most important are obviously the proportion of alkali to cellulose and the length of time they are in contact before being treated with carbon disulphide. An excess of alkali beyond the 'normal' proportion--viz. 2NaOH per 1 mol. C_{6}H_{10}O_{5}--has little influence upon the viscose reaction, but lowers the viscosity of the solution of the sulphocarbonate prepared from it. But this effect equally follows from addition of alkali to the viscose itself. The alkali-cellulose changes with age; there is a gradual alteration of the molecular structure of the cellulose, of which the properties of the viscose when prepared are the best indication. There is a progressive loss of viscosity of the solution, and a corresponding deterioration in the structural properties of the cellulose when regenerated from it--especially marked in the film form. In regard to viscosity the following observations are typical:-- (a) A viscose of 1.8 p.ct. cellulose prepared from an alkali-cellulose (cotton) fourteen days old. (b) Viscose of 1.8 p.ct. cellulose from an alkali-cellulose (cotton) three days old. (c) Glycerin diluted with 1/3 vol. water. a b b c Diluted with equal vol. water Times of flow of equal volumes from 112 321 103 170 narrow orifice in seconds